Home ProductsZinc Flake Coating

ISO9001 Corrosion Protection Combined Zinc Flake Coating

Certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
Customer Reviews
Happy to meet you in Junhe, Conny. Thanks for your professional introduce of zinc flake coating paint.I will test the sample soon.

—— GANESH ENTERPRISE

Professional team, attentive service , delivery so fast , and we will continue to cooperation with Junhe bearing company!!!

—— Mahyar Tasbihi

I'm Online Chat Now

ISO9001 Corrosion Protection Combined Zinc Flake Coating

ISO9001 Corrosion Protection Combined Zinc Flake Coating
ISO9001 Corrosion Protection Combined Zinc Flake Coating
ISO9001 Corrosion Protection Combined Zinc Flake Coating ISO9001 Corrosion Protection Combined Zinc Flake Coating

Large Image :  ISO9001 Corrosion Protection Combined Zinc Flake Coating

Product Details:
Place of Origin: Changzhou in China
Brand Name: GAT
Certification: ISO9001
Model Number: JH-9382
Payment & Shipping Terms:
Minimum Order Quantity: 100 Kiloamperes
Price: Negotiable
Packaging Details: A16KG/B24kg
Delivery Time: Ten days after receipt of advance payment
Payment Terms: L/C, T/T
Supply Ability: 2 Ton/Tons per Day

ISO9001 Corrosion Protection Combined Zinc Flake Coating

Description
PH (20℃): 3.8-5.2 Cr6+: ≥25g/L
Specific Gravity: 1.33±0.05(dip-spin Coating) Viscosity: 20-60seconds(spraying)
Operating Temperature: 22±2℃ Name: Zinc Flake Coating
High Light:

corrosion protection Zinc Flake Coating

,

corrosion protection dip spin Coating

,

ISO9001 Zinc Flake Coating

 

Dip Spin Zinc Flake Coating With Microlayer Corrosion Protection

 

1 Zinc Flake Coating Information

 

Trade Name: Zincover

Article/Model No.:JH-9382

 

 

2 Composition/information on ingredients

JH-9382 is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.

Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

3 Coating Process

3.1 Mix Ratio

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

3.2

Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

3.3

Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.

3.4

Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.

3.5

The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

v

3.6

Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

3.7

Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.

5 Technical data

 

 

No. Item Data
1 PH 3.8-5.2
2 Cr6+ ≥25g/L
3 Specific gravity 1.33±0.05( spraying)1.33±0.05(dip-spin coating)
4 Viscosity 20-60seconds(spraying) 60-80seconds(dip-spin coating) According to the different configuration of the processing workpiece viscosity
5 Operating temperature 20±2℃

 

 

6 Mix Diagram

Caution: Temperature should be controlled in above operation.

 

7 Packing

Pack A: 16kg/ Metal Barrel Pack B: 24kg Plastic Barrel Pack C: 5kg metal barrel

(For special packaging)

 

10 Quality guarantee period

Before compound 6 months at 20℃

After compound 30 days at 20℃ ( It can be recycled if adding fresh coating continuously. )

It should be stored under 20℃ if not in use.

 

ISO9001 Corrosion Protection Combined Zinc Flake Coating 0

 

ISO9001 Corrosion Protection Combined Zinc Flake Coating 1

 

ISO9001 Corrosion Protection Combined Zinc Flake Coating 2