Low Friction Zinc Flake Coating / Zinc Nickel Plating Good Heat Resistance JH-9610

JH-9610is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
 
 
Performance Charcteristic:
 
1. Chrome free
2. Good surface finish performance,high anti-corrosion,low friction coefficient.
3. No hydrogen brittleness,no pickling process.
4. Good heat resistance.
5. Good SST hours ,anti-aging cycle is long, can coat more products under the same process conditions.
 
Coating Process: 
 
1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )
 
2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
 
3. Add B to the stirring A slowly.
 
4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 20℃, otherwise C will not be dissolved sufficiently .)Then stir 10~12 hours alowly and continuously.
 
 
Technical data:
 

 
 
Mix Diagram:
 

 
Caution: Temperature should be controlled in above operation.
 
 
Coating Process:
 

 
 
Our Service

1. OEM Manufacturing welcome: Product, Package...
2. Sample order
3. We will reply you for your inquiry in 24 hours.
4. after sending, we will track the products for you once every two days, until you get the products. When you got the goods, test them, and give me a feedback.If you have any questions about the problem, contact with us, we will offer the solve way for you.