Product Details:
|
PH (20℃): | 3.8-5.2 | Cr6+: | ≥25g/L |
---|---|---|---|
Specific Gravity: | 1.33±0.05 (spray Coating) 1.33±0.05(dip-shin Coating) | Viscosity: | 20~60s(Spray Coating) |
Operating Temperature: | 22±2℃ | Name: | Zinc Flake Coating |
High Light: | Zinc Nickel Plating,Mechanical Zinc Plating |
Low Friction Zinc Flake Coating With Corrosion Protection Performance
1 Zinc Flake Coating Information
Trade Name: Zincover
Article/Model No.:JH-9510
2 Composition/information on ingredients
JH-9310 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
3 Technical data
No. | Item | Data |
1 | PH | 3.8-5.2 |
2 | Specific gravity | 1.33±0.05 (spray coating) 1.33±0.05(dip-shin coating) |
3 | Viscosity | 20~60seconds(spray coating) 60-80seconds(dip-shin coating) |
4 | Operating temperature | 20±2℃ |
4 Mix Diagram
Caution: Temperature should be controlled in above operation.
5 Coating Process
5.1 Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.
5.2 Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.
5.3 Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.
5.4 Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)
5.5 Curing
The workpiece after pre-heating should be cured at 310-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)
6 Attentions
Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .
It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.
The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.
Dedicated to strict quality control and thoughtful customer service, our experienced staff members are always available to discuss your requirements and ensure full customer satisfaction. We also welcome OEM and ODM orders. Whether selecting a current product from our catalog or seeking engineering assistance for your application, you can talk to our customer service center about your sourcing requirements.
We warmly welcome customers from at home and abroad to establish cooperation and create a bright future with us together.
Contact Person: Mrs. June
Tel: +86 13915018025
Fax: 86-519-85913023