Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness

Certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
Customer Reviews
Happy to meet you in Junhe, Conny. Thanks for your professional introduce of zinc flake coating paint.I will test the sample soon.

—— GANESH ENTERPRISE

Professional team, attentive service , delivery so fast , and we will continue to cooperation with Junhe bearing company!!!

—— Mahyar Tasbihi

I'm Online Chat Now

Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness

Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness
Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness

Large Image :  Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness

Product Details:
Place of Origin: Changzhou in china
Brand Name: JUNHE
Certification: ISO9001 SGS
Model Number: JH-9320
Payment & Shipping Terms:
Minimum Order Quantity: 100Kiloamperes
Price: US $6.3 - 6.8 / Kiloampere
Packaging Details: 15kg/ Metal Barrel
Delivery Time: Ten days after receipt of advance payment

Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness

Description
Supply Ability: 2 Ton/Tons Per Day Main Raw Material: Water-based Inorganic Silica
Color: Silver Coating Thickness(μ): First Coating≥15
Flexibility(mm): ≤3 Non-volatile: %30
Adhesion: ≤ 2 Hardness: 0.7
Impact Resistance(KG.CM): 50 Wet And Heat: 240h
High Light:

Anti Corrosion Coating

,

Zinc Nickel Plating

 
 
Product Description:
 

Our for zinc flake coating surface hardness is low, defects in the coating and acid and alkali resistant, draw lessons from domestic formula technology, high-quality raw materials research and production of JH-9320 zinc flake coating special self dry coating liquid, both increase of zinc flake coating on surface hardness, acid and alkali resistance, and can improve the anticorrosion performance of the coating and with zinc flake coating affinity good adhesion.
The main ingredient is water-base inorganic silica , mixed with corrosion protection assistant.The product cost is low.
 
Technical Data:

No.ItemData
1ColorSilver
2coating thickness(μ)First coating≥15
3non-volatile %30
4Adhesion≤2
5Flexibility(mm)≤3
6hardness0.7
7impact resistance(KG.CM)50
8wet and heat(h)240

 
Instructions and attention:
Dip coating,Spray coating etc.
It should be stirred fully befor usage; distilled water or deionized water can be used to adjust viscosity ;Operating viscosity:30-60s.
When the environment humidity higher than 85%,can add certain industrial alcohol to adjust viscosity
Curing condition: 80℃/10min+140℃/30min
Cleaning appliance: running water can be used
Avoid acid substances, or polymerization and deterioration will happen.
 
This product can be used alone,the coated surface request oil free,dust free and dry,the better make pre-treatment of degreasing,derusting,and phosphating.
 
Processing method:
A 1 base-coat+ 1 Top coat
 
B 2 base-coat+ 1 Top coat (heavy corrosion protection)
Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness 0
 
 
Process Parameter:
Dip Coating Temperature RT
Operateing Viscosity 45-60 S
Centrifuge 210~270 RPM/min 10s X 4-8 times
( Centrifuge device can not be mix used with spin dyrer )
Spray Coating Temperature RT
Operateing Viscosity 30~40 S
Curing: 80℃ 10min + 140℃ 20—30min
Corrosion protection of b process flow
Corrosion resistance: ≥1500h (NSS)
 
Sea water resistance: 25℃≥1500h
 
 
 
Self Dry Silver Top Coat Zinc Flake Coating 2 Adhesion Increase Surface Hardness 1

Contact Details
Changzhou Junhe Technology Stock Co.,Ltd

Contact Person: Mrs. June

Tel: +86 13915018025

Fax: 86-519-85913023

Send your inquiry directly to us (0 / 3000)