Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2

Certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
Customer Reviews
Happy to meet you in Junhe, Conny. Thanks for your professional introduce of zinc flake coating paint.I will test the sample soon.

—— GANESH ENTERPRISE

Professional team, attentive service , delivery so fast , and we will continue to cooperation with Junhe bearing company!!!

—— Mahyar Tasbihi

I'm Online Chat Now

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2
Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2
Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2

Large Image :  Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2

Product Details:
Place of Origin: Changzhou in china
Brand Name: JUNHE
Certification: ISO9001 TS16949
Model Number: JH-9380
Payment & Shipping Terms:
Minimum Order Quantity: 100 Kilograms
Price: Negotiable
Packaging Details: Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2

Description
Cr6+: ≥25g/L Color: Silver
PH: 3.8-5.2 Specific Gravity: 1.33±0.05( Spraying)1.33±0.05(dip-spin Coating)
Viscosity: 20~60s(Spray Coating) 60~90S(Dip-Spin Coating) Operating Temperature: 20±2℃
High Light:

Dip Spin Coating

,

Zinc Aluminium Flake Coating

Water base dacromet coating with good leveling adhesion PH value is 3.8-5.2
 
Product Description
 

JH-9380is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.

Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

 

Performance characteristics:

 

The film is silver white, good surface finish, high corrosion resistance, good coating.

 

Coating Process:

 

1. Mix Ratio

 

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

 

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

 

3. Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.

 

4. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.

 

5. The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

 

6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 20±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

 

7. Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.

 

Technical data:

 

No. Item Data
1 Color Silver
2 Coating method Dip Spin & Spraying
3 PH 3.8-5.2
4 Cr6+ ≥25g/L
5 Specific gravity 1.33±0.05( spraying)1.33±0.05(dip-spin coating)
6 Viscosity 20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
7 Operating temperature 20±2℃

 

 

Mix Diagram:

 

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 0

 

 

Coating Process:

 

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 1

 

 

Attentions:

 

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

 

 

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 2

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 3

 

Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2 4

 

 

Contact Details
Changzhou Junhe Technology Stock Co.,Ltd

Contact Person: Mrs. June

Tel: +86 13915018025

Fax: 86-519-85913023

Send your inquiry directly to us (0 / 3000)