Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
China Changzhou Junhe Technology Stock Co.,Ltd certification
Customer Reviews
Happy to meet you in Junhe, Conny. Thanks for your professional introduce of zinc flake coating paint.I will test the sample soon.

—— GANESH ENTERPRISE

Professional team, attentive service , delivery so fast , and we will continue to cooperation with Junhe bearing company!!!

—— Mahyar Tasbihi

I'm Online Chat Now

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Large Image :  Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Product Details:
Place of Origin: Changzhou in china
Brand Name: JUNHE
Certification: ISO9001 TS16949
Model Number: 310B
Payment & Shipping Terms:
Minimum Order Quantity: 100 Kilograms
Price: Negotiable
Packaging Details: Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Description
Color: Silver PH: 3.8-5.2
Specific Gravity: 1.30±0.05 Viscosity: 20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
Cr6+: ≥25g/L Name: Zinc Coating
High Light:

Dip Spin Coating

,

Zinc Aluminium Flake Coating

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

 

 

Dacromet anti-corrosion coating characteristics

 

1.1 anti-corrosion mechanism Dacromet coating, the appearance of matte silver gray, from the very fine sheet metal zinc, aluminum and chromate and other ingredients. After the workpiece in the degreasing, shot blasting treatment, dip Tu Duo Luo liquid.

Dacromet liquid is a water-based treatment solution, metal parts in the water-based treatment solution dip or spray, and then into the furnace curing, about 300 ℃ baking film, and the formation of zinc, aluminum, chromium inorganic coating Floor.

 

2. Coating Process

 

Mix Ratio

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

 

3


Mixture Method

Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3.2.2

Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.

 

 

4. Technical data

 

No. Item Data
1 PH 3.8-5.2
2 Cr6+ ≥25g/L
3 Specific gravity 1.30±0.05
4 Viscosity 20~60s(Spray Coating) ; 60~90S(Dip-Spin Coating) . 20℃ Zahn 2# cup
5 Operating temperature 22±2℃

 

 

 

5. Coating Process

 

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating 0

 

6.1 Degreasing

 

The workpiece should be degreased if there is oil on the surface. There are three processing methods:

1.High temperature

2.Neutral water-base degreasing agent

3.Organic solvent such as methylene chloride.

 

6.2 Derusting

The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.

 

6.3 Coating

The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.

 

6.4 Pre-heating

The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)

 

6.5 Curing

The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)

 

 

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating 1

 

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating 2

 